[产品介绍]

[Product Introduction]

有无机富锌底漆和有机富锌底漆2型，每类根据含锌量等分3型，分别满足不同程度的防腐重防腐要求。

There are two types of inorganic zinc rich primer and organic zinc rich primer, each of which is divided into three types based on the zinc content, meeting different degrees of anti-corrosion and heavy anti-corrosion requirements.

[案例]

case

荆州北闸水利工程/淮北东岗楼立交桥(中铁四局)/海南环西铁路/杭州广厦天都城仿埃菲尔铁塔

Jingzhou Beizha Water Conservancy Project/Huaibei Dongganglou Overpass (China Railway Fourth Bureau)/Hainan West Ring Railway/Hangzhou Guangxia Tiandu City imitates the Eiffel Tower。

[主要组成]

[Main components]

该产品是以中分子环氧树脂、特种树脂、锌粉、助剂和无铅溶 剂等组成的漆料为乙组份，另一组份为聚酰固化剂的双组份自 干涂料。

This product is a two-component self drying coating composed of medium molecular weight epoxy resin, special resin, zinc powder, additives, and lead-free solvents as component B, and another component as a polyacrylic curing agent.

[主要特性]

[Main Characteristics]

富含锌粉，锌粉的电化学保护作用使涂膜具有十分突出的防锈 性能；漆膜硬度高；耐高温，不影响焊接性能；干燥性能超 群；高附着力，良好的机械性能。

Rich in zinc powder, the electrochemical protection effect of zinc powder makes the coating have outstanding anti rust performance; High hardness of paint film; High temperature resistance without affecting welding performance; Excellent drying performance; High adhesion and excellent mechanical properties.

[主要用途]

[Main purpose]

广泛用于冶金、集装箱、各类交通车辆、工程机械钢板预处理 抛丸，特别适合于钢结构防腐使用，是理想的金属预处理抛丸 和防锈保养底漆。

Widely used in metallurgy, containers, various transportation vehicles, engineering machinery steel plate pre-treatment shot blasting, especially suitable for anti-corrosion use of steel structures, it is an ideal metal pre-treatment shot blasting and rust prevention maintenance primer.

[执行标准]HG/ T 3668-2009

[Execution Standard] HG/T 3668-2009

【技术指标】

Technical indicators

不挥发分：≥70%不会发分中含锌量：60

Non volatile matter: ≥ 70%. Zinc content: 60%

干燥时间：表干≤2h,实干≤24h作防锈底漆

Drying time: surface drying ≤ 2h, actual drying ≤ 24h for rust proof primer

耐冲击性：50cm

Impact resistance: 50cm

附着力(划格法):1级

Adhesion (grid method): Level 1

耐盐雾：200h(60)400h(70)600h(80)

Salt spray resistance: 200h (60) 400h (70) 600h (80)

干膜厚度55±5 μm

Dry film thickness 55 ± 5 μ m

[ 包 装 规 格 ] 2 9 k g / 组 ( 漆 ： 固 化 剂 = 2 5 : 4 )

[Packaging Specification] 2 9 kg/set (Paint: Curing Agent=2 5:4)

[配套用漆]

[Supporting paint]

各色聚氨酯漆，各色环氧面漆，各色氯化橡胶防面漆，各色丙  烯酸聚氨酯面漆，氟碳面漆

Various colors of polyurethane paint, various colors of epoxy topcoat, various colors of chlorinated rubber topcoat, various colors of acrylic polyurethane topcoat, fluorocarbon topcoat。

[注意事项]

[Precautions]

①施工前先阅读使用说明；

① Read the instructions before construction;

②用前将漆料与固化剂按要求配比调好，用多少配多少，搅拌 均匀后使用，常温25℃情况下，6小时内用完；

② Before use, mix the paint and curing agent according to the required ratio, mix as much as needed, stir evenly before use, and use within 6 hours at room temperature of 25 ℃;

③施工过程保持干燥清洁，配漆后固化剂包装桶必须盖严，以 免胶凝；

③ During the construction process, keep it dry and clean. After painting, the curing agent packaging bucket must be tightly covered to prevent gelation;

施工及干燥期间，相对湿度不得大于5%,本产品涂装后须 1天后才能交付使用；

During construction and drying, the relative humidity should not exceed 5%. This product can only be delivered for use after one day of coating;

⑤富锌底漆表面易形成锌盐，在涂装后道漆之前不应长时间暴 露。如较长间隔涂装，建议采用云铁防中间漆。

⑤ The surface of zinc rich primer is prone to the formation of zinc salts, and should not be exposed for a long time after painting. If painting at longer intervals, it is recommended to use cloud iron anti intermediate paint.